Thermoelectric Properties of Indium-Selenium Nanocomposites Prepared by Mechanical Alloying and Spark Plasma Sintering

Abstract

Indium-selenium-based compounds have received much attention as thermoelectric materials since a high thermoelectric figure of merit of 1.48 at 705 K was observed in In4Se2.35. In this study, four different compositions of indium-selenium compounds, In2Se3, InSe, In4Se3, and In4Se2.35, were prepared by mechanical alloying followed by spark plasma sintering. Their thermoelectric properties such as electrical resistivity, Seebeck coefficient, and thermal conductivity were measured in the temperature range of 300 K to 673 K. All the In-Se compounds comprised nanoscaled structures and exhibited -type conductivity with Seebeck coefficients ranging from -159 V K-1 to -568 V K-1 at room temperature.