Rapid Sintering of FeAl by Pulsed Current Activated Heating and its Mechanical Properties

Abstract

Nanopowder of FeAl was synthesized by high energy ball milling. Using the pulsed current activated sintering method, a dense nanostuctured FeAl was consolidated within 2 minutes from mechanically synthesized powders of FeAl and horizontally milled powders of Fe+Al. The grain size and hardness of FeAl sintered from horizontally milled Fe+Al powders and high energy ball milled FeAl powder were 150 nm, 50 nm and 466 kg/mm(2), 574 kg/mm(2), respectively.